ASTM 304, 316, 317, 904, 2205 Stainless Steel Plate for Industry and Building Sheet

Liao cheng si he stainless steel material limited company1CommodityStainless Steel Sheets2Material201, 202 ,304 ,304L ,316 ,316L ,309S,310S ,317L ,321, 409, 409L, 410,
420, 430, etc3Surface2B, BA, HL, 4K, 6K, 8K ,NO.1, NO. 2, NO.4, SB4StandardAISI, ASTM, DIN, EN, JIS, etc5Specification(1) thickness: 3.0mm- 16.0mm
(2) Width: 1000mm-2000mm
(3) Length: 2000mm, 2438mm, 3000mm, 6000mm, etc
(4) The specifications can be provided as clients' requirement.6Application(1) Construction, decoration
(2) petroleum, chemical industry
(3) electrical appliances, automotive, aerospace
(4) house ware, kitchen appliances, cutlery, foodstuff
(5) surgical instrument7Advantage(1) High surface quality, clean, smooth finish
(2) Good corrosion resistance, durability than ordinary steel
(3) High strength and to deform
(4) Not easy to be oxidized
(5) Good welding performance
(6) The use of diversity8Package(1) Products are packed and labeled according to regulation
(2) According to customers' requirement9Deliverywithin 20 working days since we get the deposit,
mainly according to your quantity and the ways of transportation10PaymentT/T, L/C11ShipmentFOB/CIF/CFR12Productivity500tons/month13NoteAny size can be customized as requirement.
Applications: Construction and decorationpecificationSteel GradeC%Si%Mn%P%S%Cr%Ni%Mo%Ti%OTHERMax.Max.Max.Max.Max.JISSUS3010.15120.0450.0316.00-18.006.00-8.00

G4303SUS3020.15120.0450.0317.00-19.008.00-10.00

G4304SUS3040.08120.0450.0318.00-20.008.00-10.50

G4305SUS304L0.03120.0450.0318.00-20.009.00-13.00

G4312SUS304J30.08120.0450.0317.00-19.008.00-10.50
Cu:1.00-3.00
SUH3090.2120.0450.0322.00-24.0012.00-15.00
SUS309S0.08120.0450.0322.00-24.0012.00-15.00
SUH3100.251.520.0450.0324.00-26.0019.00-22.00
SUS310S0.081.520.0450.0324.00-26.0019.00-22.00
SUS3160.08120.0450.0316.00-18.0010.00-14.002.00-3.00

SUS316L0.03120.0450.0316.00-18.0012.00-15.002.00-3.00

SUS3170.08120.0450.0318.00-20.0011.00-15.003.00-4.00

SUS3210.08120.0450.0317.00-19.009.00-13.00
5*C Min.
SUS3470.08120.0450.0317.00-19.009.00-13.00
Nb:10*C Min.
SUSXM70.08120.0450.0317.00-19.008.50-10.50
Cu:3.00-4.00
SUH4090.08110.040.0310.50-11.75
6*C to 0.75
SUH409L0.03110.040.0310.50-11.75
6*C to 0.75
SUS4100.15110.040.0311.50-13.50
SUS420J10.16-0.25110.040.0312.00-14.00
SUS420J20.26-0.40110.040.0312.00-14.00
SUS4300.120.7510.040.0316.00-18.00
SUS4340.12110.040.0316.00-18.00
0.75~1.25



ASTM Specification



SpecificationSteel GradeC%Si%Mn%P%S%Cr%Ni%Mo%Ti%OTHERMax.Max.Max.Max.MaxASTMS301000.15120.0450.0316.00-18.006.00-8.00
N:0.10 MaxA240S302000.150.7520.0450.0317.00-19.008.00-10.00
N:0.10 Max
S304000.080.7520.0450.0318.00-20.008.00-10.5
N:0.10 Max
S304030.030.7520.0450.0318.00-20.008.00-12.00
N:0.10 Max
S309080.080.7520.0450.0322.00-24.0012.00-15.00
S310080.081.520.0450.0324.00-26.0019.00-22.00
S316000.080.7520.0450.0316.00-18.0010.00-14.002.00-3.00
N:0.10 Max
S316030.030.7520.0450.0316.00-18.0010.00-14.002.00-3.00
N:0.10 Max
S317000.080.7520.0450.0318.00-20.0011.00-15.003.00-4.00
N:0.10 Max
S321000.080.7520.0450.0317.00-19.009.00-12.00
5*(C+N) Min.N:0.10 Max
0.70 Max
S347000.080.7520.0450.0317.00-19.009.00-13.00
Cb:10*CM in.
1.00 Max
S409100.03110.0450.0310.50-11.700.5Max
Ti:6*CMin.
0.5 Max.
S410000.15110.040.0311.50-13.500.75Max
S430000.12110.040.0316.00-18.000.75Max
General Properties
Alloy 304L a T-300 series stainless steel austenitic, which has a minimum of 18% chromium and 8% nickel. Type 304L has a carbon maximum is 0.030. It is the standard "18/8 stainless" that is commonly found in pans and cooking tools. Alloys 304L is the most versatile and widely used alloy in the stainless steel family. Ideal for a wide variety of home and commercial applications, Alloys 304L exhibits excellent corrosion resistance and has a high ease of fabrication, outstanding formability. The austenitic stainless steels are also considered to be the most weldable of the high-alloy steels and can be welded by all fusion and resistance welding processes.
Specifications: UNS S30403
Applications:
Alloy 304L Stainless Steel is used in a wide variety of home and commercial applications, including:
Food processing equipment, particularly in beer brewing, milk processing, and wine making
Kitchen benches, sinks, troughs, equipment, and appliances
Architectural trim and molding
Automotive and aerospace structural use
Construction material in large buildings
Chemical containers, including for transport
Heat exchangers
Nuts, bolts, screws, and other fasteners in the marine environment
Dyeing industry
Woven or welded screens for mining, quarrying & water filtration
Standards:
ASTM/ASME: S30403
EURONORM: 1.4303
AFNOR: Z2 CN 18.10
DIN: X2 CrNi 19 11
Corrosion Resistance:
Resistance to corrosion in oxidizing environments is a result of the 18 to 19% chromium that the 304 alloys contain.
Resistance to moderately aggressive organic acids is a result of the 9 to 11% nickel that the 304 alloys contain.
At times, alloy 304L may show a lower corrosion rate than the higher carbon Alloy 304; otherwise, the 304, 304L, and 304H may be considered to perform uniformly in most corrosive environments.
Alloy 304L is preferred for use in environments sufficiently corrosive to cause intergranular corrosion of welds and heat-affected zones on susceptible alloys.
Heat Resistance:
Good oxidation resistance in intermittent service to 1600°F and in continuous service to 1690°F.
Continuous use of 304 in the 800-1580°F range is not recommended if subsequent aqueous corrosion resistance is important.
Grade 304L is more resistant to carbide precipitation and can be heated into the above temperature range.
Properties of 304 Alloy
Welding Characteristics:
Excellent welding properties; post-weld annealing is not required when welding thin sections. Two important considerations in producing weld joints in the austenitic stainless steels are:
preservation of corrosion resistance
avoidance of cracking
Processing - Hot Forming:
To forge, heat uniformity to 2100 / 2300 °F
Do not forge below 1700 °F
Forging can be air cooled without danger of cracking
Processing - Cold Forming:
Its austenitic structure allows it to be deep-drawn without intermediate annealing, Making this the stainless steel grade of choice in the manufacturing of sinks, hollow-ware and saucepans.
These grades work harden rapidly. To relieve stresses produced in severe forming or spinning, parts should be full annealed or stress relief annealed as soon as possible after forming.
Machinability:
The use of chip breakers is advised since the chips can be stringy. Stainless steel work harden rapidly, heavy positive feeds, sharp tooling, and a rigid set-up should be used.of cut below the work-hardened layer resulting from the previous passes.Chemical Properties:CMnSiPSCrNiN304L0.03max2.0max0.75max0.45max0.03maxmin: 18.0 max: 20.0min: 8.0 max: 12.00.10 maxMechanical Properties:GradeTensile Strength ksi (min)Yield Strength 0.2% ksi (min)Elongation %Hardness (Brinell) MAXHardness (Rockwell B) MAX304L70254020192Physical Properties:Density
lbm/in3Thermal Conductivity
(BTU/h ft. °F)Electrical
Resistivity
(in x 10-6)Modulus of
Elasticity
(psi x 106Coefficient of
Thermal Expansion
(in/in)/
°F x 10-6Specific Heat
(BTU/lb/
°F)Melting
Range
(°F)at 68°F: 0.2859.4 at 212°F28.3 at 68°F289.4 at 32 - 212°F0.1200 at 68°F to 212°F2500 to 259012.4 at 932 °F39.4 at 752°F10.2 at 32 - 1000°F49.6 at 1652 °F10.4 at 32 - 1500°FFactory photos:
Stainless steel Sheet Packaging:
FAQ:
1.Q: Do you have the Stainless Steel Sheet /Coil in stock?A: We have Stainless Steel Sheet /Coilin stock ,also can produce according to your order needed:2.Q: What's the delivery time?A: Within ten days after payment.3.Q: Can I get some samples free?A: Free sample can be provided if you require to check the quality.4.Q: How can we trust you?A:Have Cooperated with big cutomers