Al/Zn Heavy Edge Single Sided Metallized BOPP Film Safe Film

metallized Polypropylene Film for Capacitor Use
Products:
Aluminum metallized polypropylene film
Alumimum metallized polypropylene safety film
Zinc Aluminum alloy metallized polypropylene film with heavy edge.
Zinc Aluminum alloy metallized popypropylene safety film with heavy edge.
Zinc Aluminum alloy metallized polypropylene film with heavy edge and garadient square resistence
Alumimun metallized polyester film
Zinc Aluminum alloy metallized polyester film with heavy ege.
Specifications of MPP Film:
Thickness: 3.6um 3.8um 4um 4.8um 5um 5.5um 5.8um 6um 6.8um 7um 7.8um 8um 9um 10um 12um
Width: 4.5-600mm 4.5, 9, 11, 19, 25, 30, 37.5, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 100, 110...600mm
Margin Value: 0.5mm, 1mm, 1.5mm, 2mm, 2.5mm
Cores
Material: Plastic
Width: Film Slit Width +or -0.2mm
Inener Diameter: 75mm+1.0mm or -0.5mm
Roll Outer Diamter
For slit widths 25.0mm up: 240+10 or -20mm
For slit widths 38.5mm up: 320=10 or -40mm
For slit widths 10.0mm up: 180+8 or -18mm
For slit widths 4.0mm up: 155+6-15mm
Rolls
Film is wound on solid cores, with the metalized layer inside.
Rolls are wound up to the specific outer diameter.
The loose end of the film is held in place of a closing sticker,
Rolls are always packed in pairs.
There is plastic foam between the rolas to protact tge electrode side.
Why choose us
1. As a national hightech enterprisem we have 23 years experience in capacitor film industry, 25 industry patents and a number of invention patents.
2. To ensure the product quality and consustency, we have obtained the ISO9001 quality system certificate and CQC product certificate. 3. We have moderb factories and purification plant, and the world firstclass production equipment and the technical team cosisted of a number of experts.
We are committed to become world class supplier!
Properties
Unit
RequirementsDensityg/cm30.905±0.005Thicknessµm3.8~15
tensileStrengthMD
(MPa)≥100
ElongationatBreakMD
(%)40~200
HeatShrinkageMD
(%)≤5(120°C,10min)
(120°C,10min)Break-dowmvoltageV/µm≥350(23°C,DC)
CoatingsquareresistanceΩ/square resistencewith heavy edgeheavy-edge area:3±1
non heavy -edge area:(6~20)
without heavy edge(2~20)
DissipationFactor-≤4x10-4(20 temperature,1KHz)RCΩF≥5x104