AISI 4140 Alloy Steel

AISI 4140 is a chromium molybdenum alloy steelspecification widely used in the oil and gas industry. Similar to gradeAISI 4130but with a slightly higher carbon content. The higher carbon content of AISI 4140 gives greater strength and heat treatment capabilities in comparison to AISI 4130, however it does have inferior weldability characteristics. AISI 4140 machines well in the supply condition of 18-22HRc.

We welcome export enquiries for AISI 4140 steel. Contact our sales office and consult ourshipping policyfor further details.

AnalysisCarbon0.38-0.43%Chromium0.80-1.10%Manganese0.75-1.00%Molybdenum0.15-0.25%Silicon0.10-0.35%Phosphorous0.035% maxNickel0.25% maxSulphur0.040% maxForm of Supply

China JT metal isAISI 4140steel supplier of round bar.Diameters can be supplied as full bar lengths or cut blanks. AISI 4130 ground steel bar can be supplied, providing a high tensile alloy steel precision ground bar to tight tolerances.

Contact our experienced sales team who will assist you with your AISI 4140 steel enquiry.

DiameterApplications

AISI 4140 is widely used for a variety of applications in the oil and gas sector. Typical applications includecomponents such as connection rods, collets, conveyor pins, gears, stem assemblies, pump shafts and tool, holders

Forging

Preheat the steel carefully, then raise the temperature to 1150-1200°C for forging. Do not forge below 850°C.

Annealing

Heat the AISI 4140 slowly to 800-850°C and allow enough time for the steel to be thoroughly heated. Coolslowly in the furnace to 480°C followed by air cooling.

Stress Relieving

When parts are heavily machined, ground or otherwise subject to cold work, stress relieving will be beneficialprior to hardening.

Hardening

AISI 4140 steel is usually supplied ready heat treated to 18-22HRC. If further heat treatment is requiredAISI 4130 steel is usually supplied ready heat treated with a hardness of 18-22HRC. If further heat treatment is requiredannealed AISI 4140 should be heated slowly to 840-875°C and after adequate soaking at this temperaturequench in oil. Temper as soon as the tools reach room temperature.

Tempering

Heat the AISI 4140 carefully to a suitable temperature selected by reference to a tempering chart or table(usually between 550-700°C, soak at the temperature for 2 hours per 25mm of ruling section, then allow to coolin air. Tempering between 250-375°C is not advised as tempering within this range will seriously reduce theimpact value.

Typical Mechanical Properties*
Tensile
KSI0.2%Proof Stress
KSIElongation
%Reduction
of Area %Hardness
HRcHardness
BrinellMin10080204018217Max13011022235Heat Treatment

Heat treatment temperatures, including rate of heating, cooling and soaking times will vary due to factors suchas the shape and size of each AISI 4140 steel component. Other considerations during the heat treatmentprocess include the type of furnace, quenching medium and work piece transfer facilities. Please consult yourheat treatment provider for full guidance on heat treatment of alloy steel.

Certification

AISI 4140 alloy steel is available with a cast and analysis certificate or a BS EN 10204 3.1 mill certificate, pleaserequest when placing any orders.

Quality Assured Supply

AISI 4140 round bar is supplied in accordance with our ISO 9001 : 2008 registration.

Contact China JT metalwith your enquiries for AISI 4130 alloy steel round bar.

Contact Shanghai Jingteng metal products Co., Ltd with your enquiries
Our Website: http:https://www.chinajtmetal.com/