China AISI 4130 Scm430 Forged Alloy Steel Bar

AISI 4130 SCM430 Forged Alloy Steel Bar

Sizes:200mm to 1000mm

1.AISI 4130 Steel Specification

CountryUSABS
BSJapanStandardASTM A29EN 10250/EN10083
BS 970JIS G4105Grades413025CrMo4/1.7218
708A25/708M25SCM430

2.ASTM 4130 Steels Chemical Composition

StandardGradeCMnPSSiCrMo
ASTM A2941300.28-0.330.40-0.600.0350.0400.15-0.350.80-1.100.15-0.25
EN10250
/EN1008325CrMo4/
1.72180.22-0.290.60-0.900.0250.035<=0.400.90-1.20.15-0.30JIS G4105SCM430/
SCM20.28-0.330.60-0.850.0300.0300.15-0.350.90-1.20.15-0.30

3. AISI Alloy 4130 Application

Commercial aircraft, aircraft engine mountsMilitary aircraftAutomotiveMachine toolsHydraulic toolsAuto racingAerospaceOil and gas industries - as forged valve bodies and pumpsAgricultural and defense industries etc.
4.Product Specifications
1.Size: 250mm to 800mm.
2.Length: follow by the requirement of customer(normal length is 3-6m).
3.Ultrasonic Test: GB/T6402-91 CLASS 3 or SEP 1921 C/C ,D/d.
4.Manufacture:EAF+LF+VD(Annealed,normalized,Quenched+Tempered,peeled,rough turned).
5.Packing details: Nude packing, sea-worthy packing.
6.Payment terms: T/T, L/C
AISI 4130 Steel Grade Heat TreatmentAnnealing of 4130 steels

Annealing of 4130 steel forgings may be carried out by transferring the part straight from the forging operation to a furnace held at a suitable temperature, around 860º C (1575 º F) for annealing, holding for a suitable time then furnace cooling. In this way a structure suitable for machining may be obtained. This treatment is best used for parts with simple shapes. If the 4130 forging is such that some sections will finish much colder than others then a uniform structure will not be obtained and for best results a spheroidizing anneal at around 750 º C (1380 º F) may be used. It is safe to say that experience alone will decide the best type of annealing treatment to be used prior to machining.

It should then be cooled in the furnace at a rate of less than 50 F per hour down to 900 F, followed by air cooling from 900 F.

Normalizing of Alloy Steel 4130

The nominal normalizing temperature for 4130 is 900 º C (1650 º F) followed by the 1600 F soak and oil quench, but production experience may necessitate a temperature either 50 º F (10 º C) above or below this figure. In fact when forgings are normalized before, for example, carburizing or hardening and tempering, the upper range of normalizing temperatures is used. When normalizing is the final heat treatment, the lower temperature range is used.

Hardening of AISI 4130 Alloy Steel

The steel 4130 should be austenitized - i.e. all micro constituents transformed to austenite - at 1500 to 1600 º F (815 to 870 º C). The actual austenitizing temperature is a function of chemical composition within the analysis range, section size and cooling method. Smaller sections of 4130 might be quenched in oil, heavier sections in water.

Tempering of 4130 Steel

The actual tempering temperature will depend on what required properties are needed. Alloy steel 4130 is tempered at between 398 ºC -565 ºC (750 F and 1050 F), depending upon the strength level desired. The lower the tempering temperature the greater the strength. However, tempering should not be carried out between 200 - 420 ºC (400 - 790 º F) to avoid the danger of embrittlement.

AISI 4130 alloy steel is a medium carbon, low alloy steel in ASTM A29 standard. ASTM 4140 steel is also commonly referred to as a chromoly steel, or chrome moly steel, containing nominally 0.28-0.33% Carbon, 0.8-1.1% Chromium and 0.15-0.25% Molybdenum. It is similar to 4140 steel which has a higher carbon level (0.28-0.33%), giving 4130 material improved weldability, at the expense of through thickness strength. With the proper heat treatment it is also readily machined. Annealing ASTM 4130 alloy steel offers excellent ductility. AISI 4130 steel is usually supplied as round bar commonly in the hardened and tempered condition.
If you have any need for SAE 4130 4140 4340 Hot rolled or Forged Steel Bars, please contact me freely.