China Amino Moulding Powder Urea Moulding Compound

GENERAL CHARACTERISTICS.

JOSEN Amino Moulding Powders are based on colourless thermosetting resins which are condensation products of either urea or melamine with formaldehyde. These resins are combined with high purity alpha cellulose filler, pigments, catalyst and other additives to give the range of materials described in our Technical Brochure.
JOSEN materials conform to internationally recognised standards. ( DIN 7708 Type 131.5 / ISO 2112/BS1322 - UFA10 / UL94 )


STABILITY
A storage of at least 6 months can be expected when stored in cool and dry conditions between 5'C and 20'C. A prolonged storage at higher temperatures will reduce the storage life of the material.

PRODUCT NAME: UREA MOULDING COMPOUND,
TYPE: UF1G-A-2007 Grade: Compression grade

PropertiesUF1G-A-2007UnitTest ResultStandard1Inflect strength( Unnotched)kJ/m27.52ISO179-1:20002Inflect strength( Notched)kJ/m21.68ISO179-1:20013Heat distortion temperature°C123ISO75-2:20034Densityg/cm31.48ISO1183-1:20045Shrinkage%0.74ISO2577:20076Post Shrinkage(80°C+/-2°C/48h)%0.54ISO2577:20077Dielectric StrengthMV/m13.7IEC60243-1:19988Insulation resistance,(after 24h in water)Ω2.7x10**12IEC60167:19649Proof Tracking Index
PTI600-0.52IEC60112:197910Glow Wire 960°C, 180sec.RatingBH2-10IEC60700:198111Oxgen Index%31.5ISO4589:198412FlammabilityRatingV-0IEC60695-11-10:2003

PRODUCT NAME: UREA MOULDING COMPOUND,
TYPE: UF1G-C-1210Z Grade: Injection grade

PropertiesUF1G-C-1210ZUnitTest ResultStandard1Inflect strength( Unnotched)kJ/m26.51ISO179-1:20002Inflect strength( Notched)kJ/m21.70ISO179-1:20013Heat distortion temperature°C130ISO75-2:20034Densityg/cm31.5ISO1183-1:20045Shrinkage%0.78ISO2577:20076Post Shrinkage(80°C+/-2°C/48h)%0.37ISO2577:20087Dielectric StrengthMV/m12.9IEC60243-1:19988Insulation resistance,(after 24h in water)Ω7.2x10**12IEC60167:19649Proof Tracking Index
PTI600-0.61IEC60112:197910Glow Wire 960°C, 180sec.RatingBH2-7IEC60707:198111Oxgen Index%33.3ISO4589:198412FlammabilityRatingV-0IEC60695-11-10:2003