Wear Resistant Pipe, Cement Plant Resistant Pipe, Cco Clad Bimetallic Plate manufacturer / supplier in China, offering Customized Big Size Wear Resistant Pipe for Cement Industry, Shovel Bucket Liners Chromium Carbide Wear Resistant Plate, Jiangsu Welldam Hardfacing Liner Plate for Cement Factory, Mining Factory, Power Station and Port and so on.
Min. Order / Reference FOB Price | |
---|---|
1 Ton | US $600.00/ Ton |
Local Area: | Jian, Jiangxi, China |
---|---|
R&D Capacity: | OEM, ODM, Other |
Payment Terms: | LC, T/T |
Standard: | JIS, GB, DIN, BS, ASTM, AISI |
---|---|
Application: | Loader, Construction Machinery, Metallurgical Machinery, Cement Plant, Mining Machine, Thermal Power |
Material: | Steel |
Bimetallic overlay cladded abrasion chromium carbide wear resistant steel
Welldam wear plate are manufactured by welding one or multiple abrasion resistant layers on a medium or low carbon steel base plate. The overlay alloy has a high amount of chromium carbide hard particles.Product NameWED Wear Resistant SteelMaterialHigh chromium carbide overlay wear resistant steel
Thickness 4+4 5+3 6+4 6+5 8+4 8+6 8+8 10+4 10+6 10+8 10+10 12+4 12+6 12+8 12+10 14+6 14+8 14+10 16+6 16+816+10 16+12, etc. or as customizedWeldable Thickness3-20mm
HardnessHRC 52-62
Wear deposite 3mm: HRC 52-58, 4mm: HRC 56-60, 5mm: HRC 58-62,
6mm: HRC 58-62, 8mm: HRC 58-62, 10mm: HRC 60-62, 12mm: >62HRC of 1st layer :52-58; HRC of 2nd layer: 58-62; HRC of Pure weld deposite: 62Surface TreatmentHardfacing clading coated.TechniqueAdvanced automatic self-shilded open arc welding
Chemical CompositionTake 6+6 wear resistant steel for example:
C : 4.3-4.8% Cr : 23-30% Mn : 0.8-1.1%Mo: 0.08-0.18 Ni:0.08-0.15
Other metal elements : Micro base PlateQ235B, All weldable steels, mostly structural steels.
FeatureHigh wear resistance
12-20 times higher than common plate
5-10 times than low alloy steel plate
2-3 times than high chromium cast iron plate