China Catalyst Carrier Ceramic Honeycomb Substrate

Ceramic Honeycomb Substrate Description:
Ceramic Honeycomb substrate is made of cordierite, and it is used for car catalytic converter. The cells density can be 100 cpsi, 300 cpsi, 400 cpsi or 600 cpsi. The shape will be round, oval or racetrack. We can supply both ceramic element coated with noble metals of Pt, Pd, Rh and ceramic element without noble metals. Ceramic Honeycomb as catalytic converter substrate low thermal expansion coefficient, good thernal shock resistance. Ceramic Honeycomb Substrate ate made of cordierite enjoys the merits of very low thermal expansion coefficient, high specific surface area, low pressure drop, rapid light-off and unique structures which are perfect for car catalytic converter. We can supply both ceramic element coated with noble metals of Pt, Pd, Rh and ceramic element without noble metals. The shape will be round, oval or racetrack with 100 cpsi, 300 cpsi, 400 cpsi or 600 cpsi cells that provide high surface for the precious metal catalysts that convert noxious emission into water vapor, carbon dioxide and so on.
Specifications
*the wall thickness
*low pressure drop
*high surface area
*height compressive strength
*low thermal expansion coefficient
The gasoline engine tail gas purifier carrier coated with catalyst is suitable for
And is currently one of the most important means to control tail gas purification
For gasoline engine discharge of tail gas in motorized vehicles. Our honeycomb
Ceramics are characterized by unique honeycomb structure, low expansion coefficient,
Good thermal stability, large specific area and low pressure loss, and reach
Domestic advanced level.
Chemical and physical properties:
*Chemical composition: Al2O3, 35.2± 1%; SiO2, 50.9± 1%; MgO 13.9± 1%
*Content of main crystal phase of cordierite: ≥ 90%
*Compression strength under normal temperature: Direction A ≥ 20MPa, directionB≥ 4MPa
*Water absorption: 23-27%
*Softening temperature: >1, 420oC
*Flame resistance: >1, 600oC
*Thermal expansion coefficient: ≤ 1.3 x 10-6/oC
*Thermal shock resistance: No crack under 650oC air-cooling
*Wall thickness: 0.17-0.20mm (400 cells/square inch), 0.12-0.15mm (600cells/squareinch)
*Volumetric weight: 0.40-0.50g/L
*Tolerance of outside dimensions: ± 1%Specifications:
*Pore density: 400 cells/square inch
*Section shape: Circular
Num Specification Holes shape Type1120 x 81 x 76.2Square400Cell/In2(CPSI)2120 x 80 x 150Square400Cell/In2(CPSI)3144 x 68 x 150Square400Cell/In2(CPSI)4125 x 80 x 100Square400Cell/In2(CPSI) Num Specification Holes shape Type1Φ 83 x 85Square400Cell/In2(CPSI)2Φ 100 x 100Square400Cell/In2(CPSI)3Φ 130 x 130Square400Cell/In2(CPSI)4Φ 118 x 150Square400Cell/In2(CPSI)5Φ 107 x 100Square400Cell/In2(CPSI)6Φ 150 x 75Square400Cell/In2(CPSI)7Φ 83 x 125Square400Cell/In2(CPSI)8Φ 150 x 150Square300Cell/In2(CPSI)9Φ 120 x 100Square300Cell/In2(CPSI)10Φ 101.6 x 100Square300Cell/In2(CPSI)11Φ 94 x 100Square300Cell/In2(CPSI)12Φ 85 x 70Square300Cell/In2(CPSI)ItemdataCFT-02(260Channel)CFT-03(300Channel)CFT-04(400Channel)CFT-06(600Channel)kg/cm ³≤ 0.70Water Absorption%20-27Resistance to normal atmospheric temperatureX(Parallel to channels)≥ 50≥ 50≥ 65Y(Vertical to channels)≥ 160≥ 180≥ 200Coefficient of Thermal Expansion ° C-1(20-800 ° C)≤ 1.50*10^6Soften temperature ° C>1450Thermal stability 800 ° C≥ 3Specific Surface Area (cm ² /cm ³ )≥ 20Chemical composition range%AI2O3SiO2MgOK.Na2OFe2O3other31-3448-5112-14<1<0.5<1Specific heat20-100 ° C J/KG.K800-900800-950800-1200750-800850-1100840-920Theraml conductivity20-100 ° C W/m.k1.5-2.51.4-2.01.5-2.51.5-1.51.5-2.31.0-1.2