China Citic IC Mill Shell Lining

CITIC IC mill shell lining
Mill Liners:Ball Mill Liners, SAG/AG Mill Liners, Rod Mill Liners
ZTIC specialized in producing wear-resist castings used in grinding equipments and main spindle bush, brake shoe for the mill of various specifications. It has strong casting, heat treatment and machining ability, strict quality and process controlled methods as well as the perfect examination and experimental means, so that can wear-resisting products enjoy high reputation in China and sells well all over the world.
GENERAL DEscriptION
Grinding wear parts are subjected to different combinations of impact and abrasion, as they are used in SAG/AG, ball or rod mills. Our wear parts are manufactured to the highest standards of quality, traceability and delivery, ensuring high levels of reliability for our customers. Also, our wear parts add value to customers' processes through customized designs The use of internationally recognized advanced specialized software simulation mill liners for lining structure, size to optimize the design.
Barrel and cap are made of wear-resistant liner material chrome molybdenum alloy steel, the use of convex liner, improve service life and grinding effect.
Liner with a flat head bolts, supporting self-locking nut and ferrule. Coupling bolts with special seals to prevent leakage of plasma.
Quantity bolted liner wealthy amount of 5%.
Cover and cylinder liner wear-resistant rubber padding junction strip, which is fixed by the close of the liner.
Rubber gasket between the cylinder liner and a thickness of 6mm, noise can be reduced.

SAG/AG Mill Liners:
Integrated and/or plate and lifter designs for head and shell liners
Grates
Pulp lifters
Filler rings
Ball Mill Liners:
Single wave liners
Modified single wave liners
Double wave liners
Shell liners
Feed head liners
Discharge end liners
Rod Mill Liners:
Shell liners
Head liners
"Wedge" shell liners
Specification for Steel Castings for Grinding Mills
Applicable Specifications
a. ASTM A609
b. ASTM A609 S1
For ASTM A 216 WCA Steel (modified):

Chemical composition
Maximum percent allowable Carbon0.24% (0.28%)
(0.28% for head and trunnion) Manganese0.90% Silicon0.30-0.45% Sulfur0.025% Phosphorus0.025% Nickel0.25% Chromium0.20% Molybdenum0.15% Cooper0.20% Vanadium0.03%

.
The intent of these modified chemical requirement is to limit the hot tear potential in the cast steel.
Acceptance Standard

TypeI II III
IV


V

Linear discontinuities
Shrinkage Inclusions

Internal Chills

Porosity

None accepted
1

Level 1
2

Level 2

All levels unacceptable
1

Level 1