L.T Graphite has a comprehensive product and technology portfolio that focuses on four fields of graphite- ultrafine particle graphitemould, graphiteelectrode, graphite crucible, as well as other products mainly made of graphite.
Graphitematerials exhibit unique properties such as good electrical and thermal conductivity, heat and corrosion resistance,low friction, and reduced weight while at the same time maintaining high strength. Due to the shortage of energy and raw materials, our high performance products made from graphiteare in increasingly high demand in industries. They also play a progressively important role in everyday life, thereby substituting traditional materials.
L.T Graphite crucible is divided into four categories: high purity fine particle graphite crucible, medium particle graphite crucible, silicon carbide graphite crucible and other coated graphite crucible(graphite crucible for vacuum coating of gasification aluminum ) Graphite cruciblehas good thermal conductivity and high temperature resistance, the use of high temperature, the thermal expansion coefficient is small, the rapid heat, quenching has a certain anti-strain properties. Right acid, alkaline solution, strong corrosion resistance, with excellent chemical stability.
Due to its excellent performance, graphite crucible is widely used in metallurgy, casting, machinery, chemical and other industrial sectors for the smelting of alloy tool steel and the smelting of non-ferrous metals and their alloys, and has good technical and economic effects.
1. High strength .As the temperature rises, the graphite strength increases
2. High temperature resistance
3. Good heat shock resistance
4. Anti-oxidation
5. Strong corrosion resistance to acid and alkali liquid
6. Good conductivity and thermal efficiency.
7. Excellent chemicaPrinting Machinery l stability
8. High heat conductivity
9. Mechanical shock resistance
10. Small thermal expansion coefficient
Density g/cm³1.75-1.9Resistivity μΩ·m≤12Compressive strength Mpa≥70Porosity %≤26Elasticity Modulus Gpa6-18Thermal expansion coefficient 10-6/ºC1.47-4.25Ash content %≤0.05TemperatEnergy Saver ure resistance ºC≤4350ºC
ItemUnit2.0mm
HNLT2.0mm
HNLTBluk Densityg/cm3≯12≯9Electric ResitivityμΩm≮1.58≮1.70Compressive StrengthMpa≮19≮30Bending StrengthMpa≮7.8≮Non Woven Bag 13Ash Content%≯0.3≯0.3C.T.E10-6/ºC≯2.0≯2.2
C.
Bulk Density g/cm³1.9-2.1Porosity %10-14Carbon Content %30-45Silicon Carbide content %≥48Temperature resistance ºC1665
d. Graphite crucible for vacuum coating of gasificatCutting & Fold-bend Machine ion aluminum for example.
Is mainly suitable for under the condition of vacuum, the metal aluminum gasificationand evaporation on the surface of CPP, PET, BOPP film, And forming aluminum composite film. Graphite crucibles are a large number of consumption parts during the producing process, the quality of graphite crucibles will directly affect the product quality and production cost of aluminum plating film.
L.T graphite has developed a new kind graphite composite materials, used for vacuum coating of gasification aluminum, with outstanding features: greatlyPre-Press Equipment improve its oxidation resistance, high bulk density and flexural compressive strength, increased abrasion resistance and hardness, reduce porosity and permeability. The wetting and erosion ability of molten aluminum liquid and gaseous aluminum molecules is weakened to a large extent, and thus the service lifeof the crucibleis prolonged.