China Fecral Resistor Strip

FeCrAl Resistance Alloy
1. Description
FeCrAl Resistance Alloy belongs to electric heating alloy. FeCrAl alloy contains a large number of chromium and aluminum elements, it has excellent high temperature oxidation resistance, its temperature can reach 1400 degrees Celsius.
2. Advantage
FeCrAl Heating alloy has also joined the rare earth elements, changing the composition of the oxide film, the organizational structure and improving the strength and ductility of the oxide film, the increase in density and adhesion, thereby enhancing the antioxidant capacity of the alloy, extended heating element life.
3. Forming
It exists in the form of strip, round wire, ribbon wire, sheet, tape, rod and plate.
4. Application
They are mainly used in electric locomotive, diesel locomotive, metro vehicle and high speed moving car etc brake system brake resistor, electric ceramic cooktop, industrial furnace.
4.1. Locomotive Resistor Alloy
The locomotive resistance strip is used in braking system of electric power, engine, subway in resistance cabinet.
The available grade: 0Cr13Al4, 1Cr15Al5
Regular size: (0.6mm--1.5mm)*(60mm--90mm)
4.2. Home Appliances
The electric heating strip is used in electric blanket, hair dryer, rice cookers, electric kettle, electric ceramic cooktop etc.
The available grade: 0Cr21Al6, 0Cr25Al5
Regular size: (0.04mm--0.1mm)*(5mm-12mm)
(0.04mm--0.1mm)*12mm(above)
4.3. Industrial Furnace Strip
The FeCrAl resistance strip is used heat treatment furnace, melting furnace, dosing and holding furnace, dental furnace, diffusion furnace, laboratory furnace.
The available grade: 0Cr13Al4, 0Cr21Al6, 0Cr25Al5, 0Cr20Al5, 0Cr23Al5
Regular size: (1.5mm--3mm)*(10mm--30mm)
4.4. FeCrAl foil for catalytic converter
The FeCrAl resistance foil is used in catalytic converter of automobile, motorcycle for purifying gas.
The available grade: 0Cr20Al5, 0Cr25Al5
Regular size: (0.06mm--0.08mm)*(10mm--30mm)

Properties/Grade1Cr13Al40Cr21Al40Cr21Al60Cr23Al50Cr25Al50Cr21Al6Nb0Cr27Al7Mo2Main Chemical composition(%)Cr12.0-15.018.0-21.019.0-22.022.5-24.523.0-26.021.0-23.026.5-27.8Al4.0-6.03.0-4.25.0-7.04.2-5.04.5-6.55.0-7.06.0-7.0FeBalanceBalanceBalanceBalanceBalanceBalanceBalanceReopportuneopportuneopportuneopportuneopportuneopportuneopportune

Nb:0.5 Mo:1.8-2.2Max.continuous service temp.of element950110012501250125013501400Resistivity at 20oC (μ Ω @ m)1.25+-0.081.23+-0.061.42+-0.071.35+-0.071.42+-0.061.45+-0.071.53+-0.07Density (g/cm3)7.47.357.167.257.17.17.1Thermal conductivity(KJ/m@ h@ ºC)52.746.963.260.246.146.145.2Coefficient of lines expansion(α x 10-6/ºC)15.413.514.715161616Melting point (approx. )( ºC)1450150015001500150015101520Elongation at rupture (%)≥16≥12≥12≥12≥12≥12≥10Micrographic structureFerriteFerriteFerriteFerriteFerriteFerriteFerriteMagnetic propertiesmagneticmagneticmagneticmagneticmagneticmagneticmagnetic