China High Density Tungsten Alloy Bar

Tungsten alloy rod is produced by pressing and sintering metal powders into billets, which are worked by rolling or swaging into rod. Smaller sizes are produced by subsequent drawing. Tungsten alloy rod is produced in straight random lengths with a smooth swaged surface at diameters 3mm and larger, and with a smooth drawn finish below 3mm. A centerless ground finish can also be furnished. Specific lengths and special fabrications can be supplied upon request.
Tungsten Alloy Rod Specifications
1, Diameter: 2.0-100.0mm (according customer required)
2, Length: 50-1000mm
3, Density: 15.8-18.75 g/cm3
4, Composition: W content: 85-99%, W-Ni-Fe, W-Ni-Cu
5, Surface: Sintering surface, Forged surface, Ground surface
Applications for Tungsten Alloy Rod
These kinds of tungsten alloy rod can be machined further into the parts of counterweights, radiation shielding, military defense appliances, welding rods, extrusion dies or radiation shielding. Some are used in sports to create darts, billets, golf club, etc. We manufacture and offer tungsten alloy rod that can be used as the substitute for Anviloy 1150, with very similar properties.
With tungsten alloy rod high density, high melting point, small capacity, excellent hardness, superior wearing resistance, high ultimate tensile strength, etc. tungsten alloy rod is increasingly popular material.

AMS-T-21014

Class 1

Class 2

Class 3

Class 4

Composition(%)

90W7Ni3Fe

93W4Ni3Fe

95W3Ni2Fe

97W2Ni1Fe

Density(g/cm3)

17.1+/-0.15

17.6+/-0.15

18.1+/-0.15

18.5+/-0.15

Tensile Strength(MPa)

900-1000

900-1000

920-1100

920-1100

Elongation(%)

18-29

16-24

10-22

6-13

Hardness(HRC)

24-28

26-30

27-32

28-36