China Invar Plate Vacodil36 Invar Alloy Plate

Invar36 foil with max width 1300mm used for CRP parts of aviation industry
ClassElectric Motor ification : low coefficient of thermal expansion alloy
Application: Invar is used where high dimensional stability is required, such as precision instruments, clocks, seismic creep gauges, television shadow-mask frames, valves in motors, and antimagnetic watches. In land surveying, when first-order (high-precision) elevation leveling is to be performed, the leveling rods used are made of Invar, instead of wood, fiberglass, or other metals. Invar struts were used in some pistons to limit their thermal expansion inside their cylinders.

Chemical Composition in %, Invar
Ni
35-37%
Fe
.
C
0.05%
Si
0.3%
Mn
0,3-0,6 %
S
o 0.015%
P
0.015%
Mo
0.1%
V
0.1%
Al
0.1%
Cu
0.1%
Cr
0,15 %
Basic physical constants and mechanical properties of the alloy:
Density: γ = 8,1 g / cm3;
Electric resistivity: ρ = 0,78 ohm mm2 ? / m;
The temperature of the Curie point: Θs = 230 ° C;
Modulus of elasticity E = 144 kN / mm2;
Linear expansion coefficient a1 (20-100 ºC) ≤1,5 * 10-6 ºC -1
Temperature Range/ºC1/10-6ºC-1Temperature Range/ºC1/10-6ºC-120~-601.820~2503.620~-401.820~3005.220~-201.620~3506.520~01.620~4007.820~501.120~4508.920~1001.420~5009.7Package & Conveyance 20~1501.920~55010.420~2002.520~60011
Typical Mechanical properties
Tensile StrengthElongationMpa%6411468997318
Temperature factor of resistivityTemperature range, ºC20~5020~10020~20020~30020~400Printing Materials aR/ 103 *ºC1.81.71.41.21.0The heat treatment processAnnealing for stress reliefHeated to 530~550ºC and hold 1~2 h. Cold downannealingIn order to eliminate hardening, which be bring out in cold-rolled, cold drawing process. AnnGPS ealing needs heated to 830~880ºC in vacuum,hold 30 min.The stabilization process
In protective media and heated to 830 ºC, hold 20min. ~ 1h, quench
Due to the stress generated by quenching, heated to 315ºC,hold 1~4h.
Precautions
Can not be hardened by heat treatment
Surface treatment can be sandblasting, polishing or pickling.
Alloy can be used 25% hydrochloric acid pickling solution at 70 ºC to clear oxidized surface