Temporary Road Mats, Road Mats, HDPE Road Mat manufacturer / supplier in China, offering UV Resistant Durable HDPE Plastic Temporary Construction Ground Road Panel Indoor Floor Protection System Mat, Heavy Duty Pipeline Excavator Construction Road Rig HDPE Composite Mat, Maintenance-Free and Anti-Aging UHMWPE Panels for Marine Port Fenders and so on.
Min. Order / Reference FOB Price | |
---|---|
100 Pieces | US $27.70/ Pieces |
Local Area: | Dezhou, Shandong, China |
---|---|
R&D Capacity: | OEM, ODM, Other |
Payment Terms: | LC, T/T, PayPal |
Material: | PE |
---|---|
Kind: | Engineering Plastic Sheet |
Water Absorption: | <0.01% |
As you can see HDPE has a diverse range of uses from manufacturing to medical as well as in wire and cable applications. This is due to its long list of benefits which meet specific requirements for many different jobs.
The advantages of HDPE include, but are not limited to:
Excellent resistance to stress and high resistant to crackingAbrasion wear resistance - 15 times more resistant to abrasion than carbon steelIts 40% Stronger than Aramid yarnsIts strong chemical resistance - highly resilient to most alkalis and acid, organic solvents, degreasing agents and electrolytic attackIt's non-toxicExcellent dielectric propertiesSelf-lubricating - very low coefficient of friction (comparable to PTFE)Non-stainingFDA approved for use in food and medical applicationsLow specific gravity - will float in waterHDPE Outrigger Pads are an alternative to wood pads due to their superior characteristics and performance which allows them to last longer.Property:
Test Method (Standard)
Ticona GUI4152
Ticona GUI4150,4120
Unit
Molecular weight
1.5million-4million
1.5million-8million
Density
ISO 1183-1:2012/DIN53479
0.92-0.98
0.93-0.98
g/cm³
Compression strength
ISO 604:2002
≥30
≥32
Mpa
Tensile strength
ISO527-2:2012
≥20
≥22
Mpa
Elongation at break
ISO527-2:2012
≥280
≥300
%
Dynamic Friction coefficient
ASTM D 1894/GB10006-88
≤0.20
≤0.18
Notched impact strength (Charpy)
ISO179-1:2010/GB/T 1043.1-2008
≥100
≥100
kJ/m2
Abrasion wear index
ES-X60210-2008
≤30
≤30
mg
Vicat softing point
ISO306:2004
≥80
≥80
°C
Hardness shore-D
ISO 868:2003
60-65
61-66
D