China RTV Silicone Liquid Molding Silicon Rubber Silicon Rubber

Description
HY-918with the advantages ofhigh temperature resistance, abrasion resistance,good printing effect, etc. ,which made of top-quality raw material due to adding American Dupont Teflon high-temperature resistance new material, is processed through high-temperature mCrane achining. The product is mainly applicable to plastics toys, electroplating products, electronic toys, trademarks and irregular pattern printing. The silicon pad is acarrier which transfer printing the patterns on the steel plate onto the toy products' surface.Application
HY-918 is akind of silicone rubber to make the printing pads for plastic toys, craft works, product printing.
Technical ParametersModelColorMixing ratio(%)Potlife (mins,
under 25ºC)Curingtime
(hrs,under 25ºC )Hardness(Wheel & Caster Shore A)Tensile-
strength(MPa)Tear-
strength (kN/m)Viscosity
(After A/B mixed ,mPa.s)Shrinkage
rate (%)Elongation
(%)HY-918Red
Yellow
green
white2-330-404-530±2
5.2±0.3
3Tools & Hardware 0±2
32000±20Hand Tools 00
≤0.3%290%
Characteristics
*good printing effects
*good quality
*good resilience
*and without any impurity.Operationinstructions
Step 1:
prepareall the tools likethe pad mold, acup for mixing, and aglass stick. Clean the pad mould with detergent, and dry the pad mould with an air-gun or cloth, then brush alay of mold release agent.Step 2:
Generally, the ratio of pad printing silicon rubberandthe silicon oil depends on the size of pattern which customer needs to print. The larger the pattern is, the softer the printing pad should be, and more silicon oil needs to add. Contrarily, if asilicon pad with high hardness needed, silicon oil should be added less or none. General hardness of the printing pad is 15A°~-25 A°. If too much silicon oil added in the silicon rubber, the printing pad will be too soft, and this will limit the printing times. For silicon oil will destroy the molecular chain of the silicon rubber, no matter how supreme quality the silicon rubber is. And therefore, the printing pad will be abrasion intolerant and solvent intolerant and easy aging.Step 3:
General mixing proportion is as follows: add 30g silicon oil into 100g silicon then hardness of 20A° printing pad we get, which is suitable for the pad printing for alloy car and other products with small patterns and contact areas. If abig contact surface or asoft silicon pad needed, the mixing proportion between the silicon and the silicon oil can be 100:30-100:50. But please note that the more silicone oil added, the softer the silicon pad will be, which will also reduce printing times, abrasion resistance and solvent resistance. Therefore, cost increase and material waste will occur.Step 4:
Relation between the amount of the curing agent added and the chemical reaction of the silicon is as follows: mix 100g silicon and30g silicon oil sufficiently and evenly, then add the curing agent which is 2%-3% of the total weight of the silicon and the silicon oil, keep stirring for 2-3 minutes, and then deair to remove the air bubbles. It is better to finish deair within 10 minutes. For if it takes too long, it may cause fast curing and affect the quality of theprintingpad.Package
25KG/drum vacuum packingfor part A+1kg/ bottle catalyst for part BShelf lifeTwelve(12) months when storedunderdry and cool place by original package under25ºC

Thank you very much for paying attention to our products.:)

We have adedicated customer service team to answer any queries you may have.

Please feel free to contact us 24/7Power Transmission Parts hours. We will manage to help to resolve any issue.

Contact Person:Monica

Free Sample is Available .

If you have any more question about liquid silicone rubber ,please feel free to contactMonicaas below:

For more information, plscontact with Ms monica at any time

Tel:+86 -0755-89212386

Mob+8618948315814

Website:www.szrl.net