China Raw Material for Magnesia Carbon Bricks

The specifications of MgO-C bricks used in different parts of EAF
ITEMunitCF-MC-8CF-MC-10CF-MC-12CF-MC-14CF-MC-18CF-MC-20MgO%≥84≥82≥80≥78≥74≥72C (+)%≥8≥10≥12≥14≥18≥20Bulk Densityg/cm3≥3.05≥3.02≥3.00≥2.97≥2.92≥2.88Apparent porosity%≤4≤4≤4≤3.5≤3.5≤3.5C.C.SMPa≥45≥40≥40≥40≥35≥30M.O.RMPa≥6≥6≥8≥8≥8≥8(1400ºC*30ms)
The specifications of MgO-C bricks used in different parts of LF
ITEMunitCF-MC-5CF-MC-8CF-MC-10CF-MC-12CF-MC-14CF-MC-16CF-MC-18MgO%≥87≥84≥82≥80≥76≥74≥72C (+)%≥5≥8≥10≥12≥14≥16≥18Bulk Densityg/cm3≥3.10≥3.08≥3.02≥3.00≥2.97≥2.95≥2.93Apparent porosity%≤5≤5≤4≤4≤3≤3≤3C.C.SMPa≥45≥45≥40≥40≥35≥35≥35M.O.RMPa≥6≥6≥8≥8≥10≥10≥10(1400ºC*30ms)
The specifications of MgO-C bricks used in different parts of converter
ITEMunitCF-MC-8CF-MC-10CF-MC-12CF-MC-14CF-MC-15CF-MC-16CF-MC-18CF-MC-20MgO%≥86≥80≥78≥76≥75≥74≥72≥70C (+)%≥8≥10≥12≥14≥15≥16≥18≥20Bulk Densityg/cm3≥3.05≥3.03≥3.00≥2.96≥2.95≥2.95≥2.92≥2.88Apparent porosity%≤4≤4≤4≤3≤3≤3≤3≤3C.C.SMPa≥45≥40≥40≥40≥35≥35≥35≥30M.O.RMPa≥6≥6≥6≥8≥8≥8≥8≥81400ºC*30ms

Brick Brief Introdution
MgO-C brick was firstly developed by Japanese in 1970s, and became one popular refractory type which is made from magnesite, graphite as raw material, resin as binder, with high pressure moulding and low temperature treatment. It was introduced to China in1980s and mushroomed. China has became the Mg-C brick producing base due to the superior natual resource (magnesite and graphite resource ) , and attracted the big of world refractory to invest in factories, including RHI, Mayerton and etc. As one compound refractory, it make magnesite good slag erosion risistance and graphite high thermal conductivity and low dilatability mixed together. Thus Mg-C brick has features of high refractoriness, good thermal shock resistance,erosion resistance, and has good performance in I&S industry, including BOF, EAF, LF.
CIMM Refractory factory Introduction:
CIMM refractory factory has passed ISO9002 certification and ISO 14001 Environmental management system certification and established long-term technological cooperation with Beijing Iron&steel institute, Wuhan scientific&technology university and Beijing scientific&technology university, based on these such strong technology background, we can provide refractory comprehensive solution and service for our clients.