China Reflective Tape Refelctive Jacket Heat Transfer Film

HIGHVIZ 4001: Silver Reflective Transfer Film, PES BackingHIGHVIZ 4001 Silver Reflective Transfer Film,Composed of micro glass beads bTime & Attendance onded to heat activated adhesive, with a transparent PETcoverto protect the reflective side during applicationor an extra plastic liner to protect the adhesive side for some products. HIGHVIZ 4001 Reflective Transfer Film can be heat applied to occupational apparel,work wear, sportswear, schooluniforms as well as different substrates to meet variousfashionrequirements. It can be also laser cuttinginto graphics, characters and LOGOsas per customers' requirements.HIGHVIZ 4001 Reflective Transfer Filmmakes people visible in darknTransmitter ess, fogand rainingweather to decrease dangers, also work as an elementin thefashion industry.PhysicalPerformance:
Retro-reflection Performance:
Initial coefficient of retro-reflection performance in cd/(lxM*2)
4001: Silver Reflective Transfer film, PESBacking
Observation
AngleEntrance Angle 5°20°30°40°TestCertificateTestCertificateTestCertificateTestCertificate0.2°523≥330537≥290476≥180274≥650.33°355 ≥250359≥200340≥170230≥601°37≥2542≥1546≥1231≥101°30′20≥1020≥720≥521≥4
Test Result of 4001 Silver ReflectiveTransfer film
1.1 Abrasion
The test sample shall be abraded in accordance with EN 530:1994, method 2, using the woolen fabric abradant. The specimens shall be measured after 5 000 cycles and at a pressure of 9 KPa.
Retro-reflection after AbrasionEntrance AngleObservation AngleMeasured value (cd/(lxM*2))Minimum requirements (cd/(lxM*2))Result 5°0.2°449100PASS1.2 Flexing
The test sample shall be flexed in accordance with EN ISO 7854:1997 method A. The specimens shall be measured after 7 500 cycles.
Retro-reflection after FlexingEntrance AngleObservation AngleMeasured value (cd/(lxM*2))Electric Motor Minimum requirements (cd/(lxM*2))Result 5°0.2°446100PASS
1.3 Folding at cold temperatures
The test sample shall be exposed and folded in accordance with ISO 4675 at a temperature of (-20 ± 1)°C.
Measurements shall be made after reconditioning to the atmosphere for at least 2 h.
Retro-reflection after Folding at cold temperaturesEntrance AngleObservation AngleMeasured value (cd/(lxM*2))Minimum requirements (cd/(lxM*2))Result 5°0.2°466100PASS
1.4 Exposure to temperature variation
Specimens of the size of 180 mm x 30 mm shall be exposed continuously to a cycle of changing temperatures:
a) for 12 h at (50 ± 2) °C immediately followed by
b) 20 h at (-30 ± 2) °C
c) Conditioning for at least 2 h in accordance with 7.1.
Retro-reflection after Temperature VariationEntrance AngleObservation AngleMeasured value (cd/(lxM*2))Minimum requirements (cd/(lxM*2))Result 5°0.2°479100PASS
1.5 Wash, Dry Clean
After 25 wash, washing procedure in accordance with ISO 6330:2000+A1:2009, method 2A, dried at (50 ± 5) °C. Entrance AngleObservation AngleMeasured value (cd/(lxM*2))Minimum requirements (cd/(lxM*2))Result 5°0.2°363100PASS
After 50wash, washing procedure in accordance with ISO 6330:2000+A1:2009, method 2A, dried at (50 ± 5) °C. Entrance AngleObservation AngleMeasured value (cd/(lxM*2))Minimum requirements (cd/(lxM*2))Result 5°0.2°291100PASSAfter 50 cycleswashing, no Breakage, detachment, discoloration
After 5 cycles dry washing, no Breakage, detachment, discoloration 1.6 Retro-reflective performance in rainfall
Samples shall be tested in accordance with Annex D of this standard. Exposure at 284mm/h water flow for 2 hours. Retro-reflection after rainfallEntrance ALCD Module ngleObservation AngleMeasured value (cd/(lxM*2))Minimum requirements (cd/(lxM*2))Result 5°12'257100PASS
The above test data is from SGS and SATRA laboratory test of HIGHVIZ received samples, final production will have ±3-5% tolerance, which is acceptable. Application