China Transfer Film Reflective Transfer Film Heat Transfer Film

HIGHVIZ 4001-NS: Silver Plotter Cutting Reflective Transfer FilmHIGHVIZ 4001-NS Silver Plotter Cutting Reflective Transfer Film,Composed of micro glass beads bonSpeaker,Trumpet & Buzzer ded to heat activated adhesive, with a transparent PETcoverto protect the reflective side during application.
HIGHVIZ 4001-NS Reflective Transfer Film can be plotter cutting or lasercuttinginto graphics, characters and LOGOsas per customers' requirements, thenheat applied to occupational apparel,work wear, sportswear, schooluniforms as well as different substrates to meet variousfashionrequirements. HIGHVIZ 4001-NS Reflective Transfer Film makes people visible in darkness, fogand rainingweather to decrease dangers, also work as an elementin thefashion industry.PhysicalPerformance: Certificate: EN ISO 20471:2013 ANSI/ISEA 107:2010 AS/NZS 1906 OKEO-TEX 100
Backing: PES
Color Available: Silver
Retro-reflection: >500cd/(lx M2)
Wash: Domestic Wash≥50 cycles@60°C (ISO 6330)
Dry Clean: ≥50circles (ISO 3175)
Spec: 2.5cm*100M/Roll, 5.0cm*100m/Roll, other size upon request.
Application: Ideal for High Visibility Work Wear, Protective Uniforms, Sportswear, School Uniforms ,Fashion Wear, Fashion Bags and so on.
Retro-reflection Performance:
Initial coefficient of retro-reflection performance in cd/(lx M2)
4001-NS: Silver Reflective Transfer film, PESBacking
Observation
AngleEntrance Angle 5°20°Electronic Instrument 30°40°TestCertificateTestCertificateTestCertificateTestCertificate0.2°523≥330537≥290476Timer & Counter ≥180274≥650.33°355 ≥250359≥200340≥170230≥601°37≥2542≥1546≥1231≥101°30′20≥1020≥720≥521≥4
Test Result of 4001-NSSilver ReflectiveTransfer film
1.1 Abrasion
The test sample shall be abraded in accordance with EN 530:1994, method 2, using the woolen fabric abradant. The specimens shall be measured after 5 000 cycles and at a pressure of 9 KPa.
Retro-reflection after AbrasionEntrance AngleObservation AngleMeasured value (cd/(lx M2))Minimum requirements (cd/(lx M2))Result 5°0.2°449100PASS1.2 Flexing
The test sample shall be flexed in accordance with EN ISO 7854:1997 method A. The specimens shall be measured after 7 500 cycles.
Retro-reflection after FlexingEntrance AngleObservation AngleMeasured value (cd/(lx M2))Minimum requirements (cd/(lx M2))Cutting & Fold-bend Machine Result 5°0.2°446100PASS
1.3 Folding at cold temperatures
The test sample shall be exposed and folded in accordance with ISO 4675 at a temperature of (-20 ± 1)°C.
Measurements shall be made after reconditioning to the atmosphere for at least 2 h.
Retro-reflection after Folding at cold temperaturesEntrance AngleObservation AngleMeasured value (cd/(lx M2))Minimum requirements (cd/(lx M2))Result 5°0.2°466100PASS
1.4 Exposure to temperature variation
Specimens of the size of 180 mm x 30 mm shall be exposed continuously to a cycle of changing temperatures:
a) for 12 h at (50 ± 2) °C immediately followed by
b) 20 h at (-30 ± 2) °C
c) Conditioning for at least 2 h in accordance with 7.1.
Retro-reflection after Temperature VariationEntrance AngleObservation AngleMeasured value (cd/(lx M2))Minimum requirements (cd/(lx M2))Result 5°0.2°479100PASS
1.5 Wash, Dry Clean
After 25 wash, washing procedure in accordance with ISO 6330:2000+A1:2009, method 2A, dried at (50 ± 5) °C. Entrance AngleObservation AngleMeasured value (cd/(lx M2))Minimum requirements (cd/(lx M2))Result 5°0.2°363100PASS
After 50wash, washing procedure in accordance with ISO 6330:2000+A1:2009, method 2A, dried at (50 ± 5) °C. Entrance AngleObservation AngleMeasureElectrode d value (cd/(lx M2))Minimum requirements (cd/(lx M2))Result 5°0.2°291100PASSAfter 50 cycleswashing, no Breakage, detachment, discoloration
After 5 cycles dry washing, no Breakage, detachment, discoloration 1.6 Retro-reflective performance in rainfall
Samples shall be tested in accordance with Annex D of this standard. Exposure at 284mm/h water flow for 2 hours. Retro-reflection after rainfallEntrance AngleObservation AngleMeasured value (cd/(lx M^2))Minimum requirements (cd/(lx M2))Result 5°12'257100PASS
The above test data is from SGS and SATRA laboratory test of HIGHVIZ received samples, final production will have ±3-5% tolerance, which is acceptable. Produtcs Pictures: