China in Stock Powder Free Medical Grade Gloves

Disposable Powder Free Medical Grade Gloves Surgical Gloves White Latex Gloves

PRODUCTION DETAILS:
---------------------------------------------------------------------------------------------------------------------
PACKAGE: CUSTOMIZED ACCORDING TO BUYER'S REQUIREMENT
PACKING: 100PCS/BOX, 10BOX/CARTON
SIZE: XS/S/M/L/XL
WEIGHT: 4.0gr/4.5gr/5.0gr/5.5gr/6.0gr/CUSTOMIZE
TOLERANCE: ±0.2gr/±1%pcs
QC: AQL1.5
PAYMENT TERM: 50% DEPOSIT, 50% BALANCE BEFORE SHIPPING

SizeXSSMLXLTotal length235±5mm235±5mm235±5mm235±5mm235±5mmHandbreadth width75±5mm85±5mm95±5mm110±5mm120±5mmlength of thumb52±2mm54±2mm57±2mm59±2mm65±2mmlength of index finger66±2mm68±2mm72±2mm74±2mm80±2mmlength of middle finger77±2mm79±2mm82±2mm85±2mm92±2mmlength of ring finger68±2mm71±2mm75±2mm77±2mm82±2mmlength of little finger52±2mm54±2mm56±2mm60±2mm64±2mm LatexPVCNitrileModifiedPhysical Indexthickness of palm0.08mm min0.08mm min0.05mm min0.08mm minthickness of fingertip0.08mm min0.05mm min0.05mm min0.05mm minthickness of wrist0.08mm min0.06mm min0.05mm min0.06mm minTensile breaking strength
Before aging14MPa min
18MPa average9MPamin
12MPa average14MPa min
18MPa average14MPa min
18MPa averageTensile breaking strength
After aging14MPa min
18MPa average9MPamin
11MPa average14MPa min
16MPa average9MPamin
15MPa averageElongation at break
Before aging650% Min
680% Average350% min
420% average500% min
580% average350% min
460% averageElongation at break
After aging500% Min
600% average300% min
360% average400% min
470% average300% min
410% average