Excellent wet adhesion acrylate emulsion for primer paintProduct description:
Silicone modified acrylate emulsion----HN-01FHN-01FAppearanceLight blue liquidSolid content29±1wt%Viscosity.Cps(25ºC)≤500cpsParticle Size(nm)80-120PH7.5-8.5Minimum Film Formation Temperature(MFT)10ºCCa2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification.Pass
Feature:1.Excellent wet adhesion
2.Good alkali resistance
3.Good permeability
4.Short drying time
Application:As a general purpose primer for the internal and external wallsVinyl acetate-acrylate emulsion catalog:HN-101AppearanceLight blue liquidSolid content47±2wt%Viscosity.Cps(25ºC)1000-4000cpsParticle Size(nm)90-150PHGlass Transition Temperature (Tg)26ºCMinimum Film Formation Temperature(MFT)22-24ºCCa2+ stability 5%CaCl2:Emulsion =1:3, 48h,
No Flocculation, No Stratification.PassHN-102AppearanceLight blue liquidSolid content48±1wt%Viscosity.Cps(25ºC)500-3000Particle Size(nm)100-180PH7.0-8.0Glass Transition Temperature (Tg)24ºCMinimum Film Formation Temperature(MFT)21-23ºCCa2+ stability 5%CaCl2:Emulsion =1:3, 48h,
No Flocculation, No Stratification.PassHN-996AppearanceLight blue liquidSolid content49±1wt%Viscosity.Cps(25ºC)500-3000Particle Size(nm)90-150PH7.0-8.0Glass Transition Temperature (Tg)22ºCMinimum Film Formation Temperature(MFT)18-20ºCCa2+ stability 5%CaCl2:Emulsion =1:3, 48h,
No Flocculation, No Stratification.PassHN-4208AAppearanceTranslucency and light blue liquidSolid content46±2wt%Viscosity.Cps(25ºC)3000-6000Particle Size(nm)60-100PH7.0-8.0Glass Transition Temperature (Tg)23ºCMinimum Film Formation Temperature(MFT)22ºCHN-4208AppearanceTranslucency and light blue liquidSolid content42±1wt%Viscosity.Cps(25ºC)1000-3000Particle Size(nm)90-120PH7.0-8.0Minimum Film Formation Temperature(MFT)7-10ºCHN-01FAppearanceLight blue liquidSolid content29±1wt%Viscosity.Cps(25ºC)≤500cpsParticle Size(nm)80-120PH7.5-8.5Minimum Film Formation Temperature(MFT)10ºCHN-314TAppearanceLight blue liquidSolid content48±1wt%Viscosity.Cps(25ºC)1000-3000Particle Size(nm)100-500PH7.0-8.0Glass Transition Temperature (Tg)-15ºCMinimum Film Formation Temperature(MFT)0ºCCa2+ stability 5%CaCl2:Emulsion =1:3, 48h,
No Flocculation, No Stratification.PassHN-519NTAppearanceLight blue liquidSolid content48±1wt%Viscosity.Cps(25ºC)100-1000Particle Size(nm)90-160PH7.0-8.0Glass Transition Temperature (Tg)-40ºCMinimum Film Formation Temperature(MFT)0ºCCa2+ stability 5%CaCl2:Emulsion =1:3, 48h,
No Flocculation, No Stratification.PassHN-340TAppearanceMilk white liquidSolid content56±1wt%Viscosity.Cps(25ºC)1000-3000Particle Size(nm)300-400PH7.0-8.0Minimum Film Formation Temperature(MFT)0ºCCa2+ stability 5%CaCl2:Emulsion =1:3, 48h,
No Flocculation, No Stratification.PassHN-332TAppearanceMilky white with ahint of greenSolid content56±1wt%Viscosity.Cps(25ºC)1000-3000Particle Size(nm)200-300PH7.0-8.0Minimum Film Formation Temperature(MFT)0ºCCa2+ stability 5%CaCl2:Emulsion =1:3, 48h,
No Flocculation, No Stratification.PassOur company:
Shandong Honour Chemical Technology Co.,Ltd, located in the middle of Shandong Peninsula.Honour is acollection ofscience, industry, trade, storage, logistics, R& D, humanities education, financing, financial services integration of the comprehensive high-tech enterprises.
Honour specilze in the operation of acrylate and its extended products.The annual production capability of the environmentally waterborne acrylic emulsion, auxiliaries and waterborne polyurethane dispersions can reach to 600,000 Tons, and there are 16,000 tons chenmical liquid storage tank and 10,000 square meters solid storage in the factory.Newbetta is the largest acrylate product supplier in Shandong, with 25,000 tons production capacity of waterborne paint, waterborne metaphysical paint and other terminal products.