Glass Fiber Warp-Knitted Sandwich Mat, Biaxial Core Complex Mat

Fiberglass Biaxial Core Complex
It is made of continuous roving oriented in 0,90 directions plus sunthetic core and chopped strand bonded with stitching ployester .
It is ideal for infusion process.General Data
Code
Weight (g/m2)0°/90°
(g/m2)PP
Core layer(g/m2)Chop Density (g/m2)Moisture content
%
Wet speed
(≤S)ES600/180/3001092330/270180300≤0.2≤60ES600/180/6001392330/270180600≤0.2≤60ES800/180/4501442412/387180450≤0.2≤60

Code

Weight (g/m2)

Chopped layer(g/m2)

PP

Core layer(g/m2)

Moisture content

Wet speed

(≤S)

S300/180/300

780

300/300

180

≤0.2

≤60

S450/180/450

1080

450/450

180

≤0.2

≤60

S600/180/600

1380

600/600

180

≤0.2

≤60

S750/180/750

1680

750/750

180

≤0.2

≤60

S300/250/300

850

300/300

250

≤0.2

≤60

S450/250/450

1150

450/450

250

≤0.2

≤60

S600/250/600

1450

600/600

250

≤0.2

≤60

S750/250/750

1750

750/750

250

≤0.2

≤60

Remarks:
Roll width:Standard width in 1250mm, 1270mm, and other sizes depends on customer's real needs, available in 200mm to 3200mm.
Packing:Fiberglass chopped core mat is usually rolled in a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.
Storage:The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15ºCto 35ºCand 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.