HDPE/LDPE/LLDPE/PVC Pond Liner of Virgin MaterialProduct IntroductionGeo-membrane is produced by amethod of three layer co-extrusion model. The raw material HDPE/LDPE/LLDPE is processed at 200°C by fusing and co extrusion, whose basic properties are kept during the producing process. The material can bear chemical erosion and is suitable for wider using temperature range with alonger using life.
Application Range
It can be widely used in areas of garbage burying, waste disposal, tail minerals storage and underground construction projects.Product Technical Specification-HDPEPropertiesTest Method
ASTMTest Value0.75mm1.0mm1.25mm1.50mm2.00mm2.50mm3.00mmThickness-mils (min.ave.)D5199Nom. (mil)
-10%Lowest Individual of 10 ValuesDensity (min.)D1505/D7920.940 g/ccTensile Properties (1)(min.ave.)D6693
Type IV*Yield Strength11 kN/m15 kN/m18 kN/m22 kN/m29 kN/m37 kN/m44 kN/m* Break Strength20 kN/m27 kN/m33 kN/m40 kN/m53 kN/m67 kN/m80 kN/m* Yield Elongation12%12%12%12%12%12%12%* Break Elongation700%700%700%700%700%700%700%Tear Resistance (Min.Ave.)D100493N125N156N187N249N311N374NPuncture Resistance (Min.Ave.)D4833240N320N400N480N640N800N960NStress Crack Resistance (2)D5397 (App.)500hr.Carbon Black Content -%D1603 (3)2.0-3.0%Carbon Black DispersionD5596note (4)Oxidative Induction Time (OIT) (Min.Ave.) (5)100 min.
400 min.(a)Standard OITD3895(b)High Pressure OITD5885Oven Aging at 85ºC(5).(6)D5721(a)Standard OIT (min.ave.) -% Retained After 90 DaysD389555%
80%(b)High Pressure OIT (min.ave.) -% Retained After 90 DaysD5885UV Resistance (7)(a)Standard OIT (Min.Ave.)D3895N.R. (8)
50%(b)High Pressure OIT (min.ave.) -% Retained After 1600 hrs (9)D5885
Workshop
Wrapping and Loading
Certificate
Contact InformationCathy ZhouShandong Dageng Project Material Co., Ltd.
Factroy :High-Tech Development Zone,Feicheng,Taian,Shandong, ChinaOffice: 1-2402,16th.Miaoling Road ,Qingdao, Shandong, ChinaTel:+86-532-58807578Fax:+86-532-80615033Phone:+86 17685790299Website :www.geosynthetic.cn
S-kype: catherine.zhou2012