E316
AWS A5.4 E316-16
Explain:
E316 is a Cr18Ni12Mo2 stainless steel electrode with titanium calcium based coating. As deposited metal is added with Mo, it has good corrosion resistance, heat resistance and crack resistance, especially against pitting corrosion of chloride ion. It can be used both AC and DC, and has excellent operation performance.
purpose:
Used for welding in organic and inorganic acid (non oxidizing acid) medium and 06Cr17Ni12Mo2 stainless steel or as dissimilar steel welding.
Chemical Composition of the deposited metal(%)
C
Mn
Si
S
P
Cr
Ni
Mo
Cu
Guaranteed value
≤0.080
0.50~2.50
≤1.00
≤0.030
≤0.040
17.0~20.0
11.0~14.0
2.0~3.0
≤0.75
actual value
0.045
1.40
0.65
0.009
0.022
19.35
12.04
2.52
0.10
Mechanical Performance of the Deposited metal(620ºCx1h)
Test item
Rm (N/mm2)
A (%)
Guaranteed value
≥520
≥25
actual value
590
46
Reference current(AC,DC+)
Electrode diameter(mm)
φ2.0
φ2.5
φ3.2
φ4.0
φ5.0
welding current(A)
40~80
50~100
70~130
100~160
140~200
Matters needing attention:
1.The electrode must be baked at 300ºC 1H before welding.
2.As far as possible the use of DC power supply, the current should not be too large.