Introduction
BE-1011W blend polyol is friendly to the ozone. It is HCFC-141b free and only formulated water as blowing agent. BE-1097W is generally used for high density decorative furniture and imitative wood foam system. BE-1097W can perform perfect surface of foam with no bubble.
Typical liquid propertiesAppearanceYellow brown viscous liquidViscosity, mPa.s at 25ºC1000~1600Specific gravity, kg/m3,at 25ºC1.05~1.10Hydroxyl value, mgKOH/g330~390Recommended proportion and process conditions BE-1011W100 (p.b.w)Isocyanate125 (p.b.w)Mould release time15-20 min.Mould temperature40~50ºCReaction data (Hand-mixing at 25ºC,Stirring speed≥2500rpm)Testing itemUnitsRangeCream timeS30~35Gel timeS65~75Tack free timeS110~130Free raise densityKg/m390~120Typical foam featureItemUnitsPropertiesCore densityKg/m3300~350Closed cell content%≥95Skin hardness cell contentShore D50~55Dimensional stability,
-30ºC,48h
70ºC,48h
%
≤0.1
≤0.1