Special Activated Carbon Made by Coal, KOH, H3po4, Hgcl2, Cuo, Physical Impregnated, ASTM, Awwa Stan

Impregnated Activated Carbon made by Coal , KOH, H3PO4, HgCl2, CuO, physical impregnated carbonASTM , AWWA standard COC report
Type: Pellet, Extruded
KOH impregnated activated carbonSize:3, or 4 mm
Basic carbon: CTC:55%, 60%,65% ,70% min
KOH impregnated carbon:7%-15% min
After impregnated:Moisture:16-18% min, Ash:16-20% min
Hardness:95% min H2S removal:0.10-0.17 g/ml min
2. H3PO4 impregnated activated carbonSize:3, or 4 mm
Basic carbon: CTC:55%, 60%,65% ,70% min
H3PO4 impregnated content:10%-15% min
After impregnated:Moisture:16-18% min, Ash:16-20% min
Hardness:95% min3. CuO impregnated activated carbon
Size:3, or 4 mm
Basic carbon: CTC:55%, 60%,65% ,70% min
CuO(95%) impregnated carbon:3-6% min
After impregnated:Moisture:16-18% min, Ash:16-20% min
Hardness:95% min
4.HgCl2 catalyst, Activated carbon catalyst, Multi-compound compositeSize:3-6 mm HgCl2:4-6.5% min
Moisture: 3% max HgCl2 lossing:3% max
5. Physical catalystImpregnated with a physical, non-chemical catalyst. It is specially made to remove gaseous
impurities such as H2S. The production process is non-polluting and environmentally friendly.
Size:3, or 4 mm
Basic carbon: CTC:55%, 60%,65% ,70% min
Physical impregnated
After impregnated:Moisture:16-18% min, Ash:16-20% min
Hardness:95% min H2S removal:0.10-0.16 g/ml minPelletized activated carbon(FCP series) package: 25, 500 kgs woven bag or kraft laminated bag.Type
CTC
adsorption
min
Iodine value
Mg/g min
Bulk density
g/l
Hardness
min
Moisture
max
Ash content
max
Pelletized activated carbon
FCP1, Size:0.8 mm,1mm, 2mm
50%,60%,70%
80%,90%,100%
110%,120%
800-1150
0.35-0.52
92%-98%
5%
8%-15%
FCP2, Size:3 mm,4mm
50%,60%,70%
80%,90%,100%
110%,120%
800-1150
0.35-0.52
92%-98%
5%
8%-15%
FCP3, Siize:5 mm,6mm,7mm
50%,60%,70%
80%,90%,100%
110%,120%
800-1150
0.35-0.52
92%-98%
5%
8%-15%