Description:
E308-16 (A102) is low carbon Cr19Ni10 stainless steel type ofelectrode with Titanium-calcium coating. It is good at excellent mechanics and intercrystalline corrosion resistance. They are available on both AC and DC. Application:
For the anti-corrosion Cr19Ni9 and 0Cr19Ni11Ti stainless steel whose temperature below 300°C when weld.
Chemical Composition Deposited metal (%)CMnSiCrNiSPMoCu≤0.080.5-2.5≤0.9018-219-11≤0.03≤0.040.75≤0.75Mechanical Properties of Deposited metalTest ItemTensile Strength
ós (Mpa)Elongation
δ5(%)Guranteed≥550≥35The anti-corrosion performance and ferrite composition should be determined between buyer and seller. Sizes & Recommended Current (AC or DC)Welding rod diameter
(mm)2.0 2.5 3.2 4.0 5.0 welding current
(A)25-5050-8080-110110-160160-200
NOTES:1. Electrodes must be baked for an hour at 250°C before welding operation. Rebaking is not allowed. 2. To operate on DC as far as possible due to the penetration is not deep enough when welding.