Virgin Material Made ASTM Standard Fish Farm Pond Liner HDPE Geomembrane

Application:GENESISsmooth HDPE geomembrane liner is widely used for canal, aquaculture, irrigation ponds and remediation liners, other liner applications include landfills, waste water treatment lagoons, oil and gas exploration, power plants, etc.•Aquaculture.Geomembrane liners can be used as fish ponds, shrimp pond and other aquacultures.
•Landfills.Bottom landfill liner, landfill sealing cover, leachate regulating pool liner, etc.
•Water Treatment System.Smooth Geomembrane is applied to the adjustment of the power plant and sewage treatment pool or water treatment system.
•Mining.HDPE Geomembrane is applied for mining industry as washing pool, pool heap leaching, heap yard, dissolving tank, storage tank, the bottom of the tailing seepage control, etc.
•Other Applications.Environment protection and sanitation, water conservancy, municipal projects, landscaping, petrochemical industry, salt industry, agriculture, etc.Project application:
Features:
•Excellent chemical resistance.
•Outstanding stress crack capacity.
•Lowest permeability.
•Excellent UV resistance.
•Stable low temperature embrittlement resistance.
•Complete width and thickness specifications complete.
•Cost effective.
•Proven performance.
•Fast deployment.
•Easy transportation.
•Meet or exceed all aspects of GRI GM13.
Technical date:
If you have special needs, please feel free to tell us.PropertiesTest Value0.75mm1.00 mm1.50 mm2.00 mmThickness - mils (min. ave.)·lowest individual of 10 valuesnom. (mil)-10%nom. (mil)-10%nom. (mil)-10%nom. (mil)-10%Density (min.)0.940 g/cc0.940 g/cc0.940 g/cc0.940 g/ccTensile Properties (min. ave.)·
yield strength·
break strength·
yield elongation·
break elongation11 kN/m
20 kN/m
12%
700%15 kN/m
27 kN/m
12%
700%22 kN/m
40 kN/m
12%
700%29 kN/m
53 kN/m
12%
700%Tear Resistance (min. ave.)93N125 N187 N249 NPuncture Resistance (min. ave.)240N320 N480 N640 NStress Crack Resistance 300 hr.300 hr.300 hr.300 hr.Carbon Black Content - %2.0-3.0%2.0-3.0%2.0-3.0%2.0-3.0%Carbon Black Dispersionnote (4)note (4)note (4)note Oxidative Induction Time (OIT)
(min. ave.)
(a) Standard OIT- or -
(b) High Pressure OIT100 min.
400 min.100 min.
400 min.100 min.
400 min.100 min.
400 min.Oven Aging at 85°C
(a) Standard OIT (min. ave.) - %
retained after 90 days- or -
(b) High Pressure OIT (min. ave.) - % retained after 90 days55%
80%55%
80%55%
80%55%
80%UV Resistance
(a) Standard OIT (min. ave.)- or -
(b) High Pressure OIT (min. ave.) - % retained after 1600 hrs N.R. (8)
50%N.R. (8)
50%N.R. (8)
50%N. R.
50%v