China 50000m3-300000m3 SAAC Production Line|AAC Block Panels|AAC Concrete Cutting Machine Dongyue

Dongyue Machinery Group are leading cement brick making machine in
China.Our brick machine has been exported to more thn 60 countries.
Oversea offices are built in India.Indoneisa.Vietam etc.We have 32 fly
ash brick making machine plant in India.They spread in Bhubaneshwar ,
Coimbatore,Rajkot,Koltata,bangalore,Indore etc.Two after sale service
centers and spare stock center are available in Ahmedabad and Bhubaneshwar .India engineers are well trainned in China and can install the
machine in
India directly.
Cooperate with Germany
Dongyue provincial enterprise technology center brings together the
domestic advanced talents,at the same time absorbed technical team
from Germany AAC-concept
Gmbh,the team of five members all have serviced for the German YTong
more than 20 years.Make the Dongyue technology research and
development capabilities in the world's advanced level in the field of
AAC
1.50000m3-300000m3 Sand AAC Production Line|AAC Block & Panels|AAC Concrete Cutting Machine Dongyue
Areated concrete brick (light brick ) is the light and porous buidling material. It has
light keeping temperature cant burn and other advantages. It can be made into many
kindsof bricks (for example: 600x200x100, 80x80x180, 240x115x53, 600x200x125 ),
theycould be used industry building and common building. They are more and more popular in the world. In the future, they will replace the Clay brick completely.
2. 50000m3-300000m3 Sand AAC Production Line|AAC Block & Panels|AAC Concrete Cutting Machine Dongyue common conception
Common concrete density is usually 1600-2400kg/m3, but Areated concrete are
500kg/m3, 600kg/m3, 700kg/m3. Main use silicon material (for example: Coal ash,
sand, Stone dust and others ), through making the material small for example sand,
they can be Used directly if has enough degree of small (for example coal ash. Mixing calcium material Lime cement water to a special slop, then add the aluminum dust and
the additive. Make the Aluminum dust and the special slop have a Chemical reflect. Then produce Hydrogen to make The concrete slop to expanding or swell, foam. Next, put them into the curing room to Concreting cutting steaming curing, last, there will bacome the
light brick, the porous rate Is 70-80%.

3. 50000m3-300000m3 Sand AAC Production Line|AAC Block & Panels|AAC Concrete Cutting Machine Dongyue advantage
1). Light weight
Areated concrete density is usually 400-700kg/m3, (according the market in produce ), same as 1/3 of clay brick and 1/5 common concrete. So use the Light brick can reduce
the weight ofThe build more, and also reduce the beam of roof and pillar press best.
Then you can see, it Can save the material and cost, it also fighting shaking.
2). Keeping temperature
It has many are porous, the delivery hearting coefficient is 0.9-0.22W/(mk), the same as
1/4 Or 1/5 of clay brick, so it is best materials now in the world.
4. 50000m3-300000m3 Sand AAC Production Line|AAC Block & Panels|AAC Concrete Cutting Machine Dongyue detailed production description
AAC block machine plant, light weight block machine, aerated concrete block machine,
AAC brick machine line, light weight brick machine, aerated concrete brick machine, autoclaved aerated concrete block machine.
1). Product weight is according to 600kg/m3 to control.
2). Annual capacity 200, 000M3.
3). Set raw material proportion: Cement 6.5%, raw lime 23%, flyash 68%, gypsum 3%, aluminum Paste powder 350G/M3.
4). Water and material rate 0.631
5). One mould product 2.88M3
6). Casting slurry cycle time 5-6 minutes, cut cycle time 5 minutes.
7). Casting slurry temperature 38-42 degree
8). Body quiet stop. Time is 1.5-2.5housr, temperature 50-90 degree, after quiet stop
body Strength is 0.15-0.18Mpa
9). Steam curing cycle time, come in and out autoclave about 0.5hour, steam curing
cycle time about is 6 hours/1.6Mpa, total 6.5 hours.
5 certification

NameUnitCement lime sandSand%55-65Cement%10-20Lime%20-30Gypsum%2-3Aluminum powder paste(600kg/m3)1/100008Water &material rate 0.65-0.75Casting system° C35-38Aluminum mixing timeS30-40