Supplier Homepage Manufacturing & Processing Machinery Building Material Making Machinery Brick Making Machine China Fully Automatic AAC Machine for 50 000-300 000cbm AAC Plant

China Fully Automatic AAC Machine for 50 000-300 000cbm AAC Plant pictures & photos

China Fully Automatic AAC Machine for 50 000-300 000cbm AAC Plant

Get Latest Price

Min. Order / Reference FOB Price
1 Set	Contact Supplier

Local Area:	Linyi, Shandong, China
R&D Capacity:	OEM, ODM, Other
Payment Terms:	LC, T/T, D/P, WesternUnion

Certification:	CE, ISO, ISO9001: 2000, Ce, SGS
Customized:	Customized
Automatic Grade:	Automatic

Contact Now Request Sample Customized Request

Favorites

Product Description

Fully Automatic AAC Machine for 50, 000-300, 000CBM AAC Plant
We are the top leader in China on manufacturing the automatic aac machine /plant Autoclaved Aerated Concrete Line(AAC) with 65% market share. We have exported our lines to different countries -- Russia, Tailand, Ukraine, Middle East and so on.
We can supply our customer for designning, production, installation, commissioning, trainning and good after-sale service.
Automatic aac machine /plant Capacity: From 25000 cubic meter to 300, 000 cubic meters per year.
Euipements: Stocking raw materials, mixing, molding, forming, cutting, evaporating and curing, crane cramp, transporting etc.
1. Product weight is according to 600kg/m3 to control.
2. Annual capacity 200, 000M3.
3. Set raw material proportion: Cement 6.5%, raw lime 23%, flash 68%, gypsum 3%, aluminum paste powder 350G/M3.
4. Water and material rate 0.631
5. One mould product 2.88M3
6. Casting slurry cycle time 5-6 minutes, cut cycle time 5 minutes.
7. Casting slurry temperature 38-42 degree
8. Body quiet stop. Time is 1.5-2.5housr, temperature 50-90 degree, after quiet stop body strength is 0.15-0.18Mpa
9. Steam curing cycle time, come in and out autoclave about 0.5hour, steam curing cycle time about is 6 hours/1.6Mpa, total 6.5 hours.

NameUniteCement lime fly ashFly ash%65-70Cement%6-15Lime%18-25Gypsum%3-5Aluminum powder paste(600kg/m3)1/100008Water &material rate 0.6. -0.65Casting system° C36-40Aluminum mixing timeS30-40Name Unit Cement lime sand Sand %55-65Cement %10-20Lime %20-30Gypsum %2-3Aluminum powder paste(600kg/m3)1/100008Water &material rate 0.65-0.75Casting system° C35-38Aluminum mixing timeS30-40