China Manual Molding Silicon Rubber

Manual Molding Silicon Rubber applications
Manual Molding Silicon Rubber is primarily intended for poly resin crafts, PU crafts, PU resin crafts, gypsum crafts, unsaturated resin crafts, lighting and candles crafts, plastic toy, stationery gifts crafts industry, a large statue Buddha, relievo furniture, furniture decorative materials, statues Buddha, artifacts copied, building decoration materials, large scale cement mold, artificial fossils Factory, Europe component factory, simulation landscapes, animals and plants sculpture, sandstone crafts and so on.
Manual Molding Silicon Rubber components
Manual Molding Silicon Rubber is a kind of flowing liquid and it contains two parts. Part A is a kind of white flowing liquid and part B is the curing agent. Remember to mix part A and part B evenly, otherwise the silicon rubber will be partly solidified and this will give birth to difficulties in your final operation. What's more, the finished moulds will meet a short life. All of these will cause a waste of silicon rubber.

Manual Molding Silicon Rubber instruction:
Add curing agent of 2%-3% at the room temperature, the Manual molding silicon rubber is still operational within 30 minutes, and in 2-3 hours.
1. Adding curing agent 1%, the Manual molding silicon rubber can still be operated within 2.5 hours and can be Demoulded after 6-8 hours.
2. Adding curing agent 2%, the Manual molding silicon rubber can still be operated within 50 minutes to 1 hour and can Be demoulded after 2-3 hours.
3. Adding curing agent 3%, the Manual molding silicon rubber can still be operated within 28 - 30 minutes and can be demoulded after 1.5-2 hours.
4. Adding curing agent 4%, the Manual molding silicon rubber can still be operated within 10 - 15 minutes and can be demoulded after 1 -1.5 hours.

Model No.ColorViscosityHardness( A )Tensil Strength (MPA)Tear Strengrh (KN/m)Elogation(%)Mixing Ratio(%)Operation Time(Hours)Curing Time(Hours)528#White25000±200028±2≥1.6≥0.7≥ 20020.52-4540#White13000±200038±2≥1.8≥0.6≥ 20020.52-4570#White48000±200070±2≥1.0≥0.5≥ 13020.52-4