China RTV2 Electronic Potting Silicone Rubber for LED Power Pack Cable

Electronic Potting Compound silicone rubber
Description
HY-9045 is a kind of low viscosity, Inherent flame resistance, two components addtion cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time.
Application
HY-9045 is suitable for bonded seal of electronic components, power module and control module, LED invertor potting, etc which requires waterproof and insulation. It can be broadly used for LED screen, Wind Power Generator, PCB, substrate, etc.
Technical Parameters

ModelColorViscosity (cps)Hardness (A°)Mixing ratioOperating
Time(min)Curing
Time(hr, 25ºC)Thermal conductivity
w(m.k)}dielectric strength(kV/mm)dielectric constant(1.2MHz)Volume resistivity(Ω.cm)coefficient of linear expansion
m/(m.k)flame retardationHY-9025Grag500±50025±51:130~604~5≥0.2≥253.0-3.3≥1.0x10*16≤2.2x10*-494-V1HY-9045Grag2500±50045±51:130~604~5≥0.2≥253.0-3.3≥1.0x10*16≤2.2x10*-494-V1HY-9055Grag3000±50055±51:130~604~5≥0.2≥253.0-3.3≥1.0x10*16≤2.2x10*-494-V1HY-9300Water clear1800±800/1:11~212~14≥0.2≥253.0-3.3≥1.0x10*16≤2.2x10*-494-V1HY-9305Water clear500±1005±31:130~604~5≥0.2≥253.0-3.3≥1.0x10*16≤2.2x10*-494-V1HY-9310Water clear500±10010±31:130~604~5≥0.2≥253.0-3.3≥1.0x10*16≤2.2x10*-494-V1HY-9320Water clear1000±10020±31:130~604~5≥0.2≥253.0-3.3≥1.0x10*16≤2.2x10*-494-V1HY-9330Water clear500±10030±31:130~604~5≥0.2≥253.0-3.3≥1.0x10*16≤2.2x10*-494-V1HY-210Transparent1800±80015±310:130~604~5≥0.2≥253.0-3.3≥1.0x10*16≤2.2x10*-494-V1HY-215Black/ Light yellow/ Red brown2500±80015±310:160~1206~12≥0.2≥253.0-3.3≥1.0x10*16≤2.2x10*-494-V1

(Pls note: the above data for this product in 25 ºC temperature, 55 percent humidity conditions, for reference. The accurate data is measured by customers when using.)
TECHNICAL GUIDELINES
1, Typical Application
HY-9045 could be applied to
- high powered electronics,
- DC/DC module and circuit board which requires heat dissipation and high temperature resistance.
-It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc. Pls put part A and part B in separate container and stir evenly before mixing the two part together.
2, Mixing Ratio: part A: part B = 1:1
3, Deaeration the mixture in vacuum pump under 0.08 MPa for 3-5 minutes.Then the mixture could be used for pouring.
4, Pls note that the thickness of the silicone affects the curing time. If the silicone used is a little thick,then the curing time will be a little longer.The temperature also affects the curing time.When in lower temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization. With temperature of 80~100ºC, the silicone will cure in 15 minutes; while in 25ºC room temperature, the silicone will cure around 8 hours.
Notes:
1.The following material may hinder the curing of GD-8055, so pls use after the test. When necessary, pls clean the application areas.
Organotin compound or Condensation silicone with organotin
Sulphur, sulfide and sulfur rubber materials.
Amine compounds as well as contains the amine materials.
Pewters solder flux
2. GD-8055 should be sealed storage.The mixture should be used up disposably to avoid causing waste.
3. GD-8055 belongs to non-dangerous goods, but keep away from mouth and eyes.
4. When it gets stratified after a period of storage, Please mix it evenly before using,which does not affect the performance.

PACKAGE:
20Kg/pail as a set (Part A 10Kg + Part B 10Kg)
SHELF LIFE AND TRANSPORTATION

1.Twelve(12) months when stored at 25C in tightly closed original packages.

2.This kind of product is non-dangerous product, which could be transported as general chemicals.

3. Storage beyond the expired date does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.