Insulation Excellent Abrasion Resistance Fabric Heat Shrink Tubing

Material(s) Description
Warp material: Polyester
Weft material:Irradiated, modified polyolefin
Coating: Modified polyolefin
Operating temperature range (3000 hours): -40°C to 125°C
Operating temperature range (1000 hours): -40°C to 150°C
Minimum recovery temperature: 110°C
Recommended recovery temperature :150°C to 200°C
Maximum storage temperature: 50°C
Standard:TL52668 TL52361 D44 1959 GMW14327
Testing organization:CTI PONYProductdescription(CL-KSD)Insidediameter(mm)D(min.)expandedassuppliedd(max.)recoveredafterheatingφ6/3-B63φ8/4-B84φ10/5-B105φ12/6-B126φ16/8-B168φ20/10-B2010φ25/12-B2512φ30/15-B3015φ35/17.5-B3517.5φ40/20-B4020φ50/25-B5025φ60/30-B6030φ70/35-B7035φ80/40-B8040φ100/50-B10050B:blackOtherspecificationscanbecustomizedPropertyTest condition(s)PerformanceThermal ageing168hrs at 125°CNo deterioration in abrasion resistance at 23°C24hrs at 125°CNo deterioration in abrasion resistance at 23°CFlammabilityMVSS 302Burning rate≤100 mm/minLow temperature flexibility4 hours at -40°C,10X diameter mandrel No crackingAbrasion resistance
(1.5Nload, 0.3mm radius metal blade,60 cpm,50mm stroke, 144 000 cycles)
EnvironmentalChamber Temperature: -35°CNo wear to underlying rubber hoseEnvironmentalChamber Temperature: 140ºCTemperature resistance
1) Test temperature 140 ºC, for 500hours
2) Remove the sample and cool it to room temperature..Thenplace the sample at -35°C for 22 hours.
3) Then bend the sample 180 degrees around a cylinder with a radius of 30mmTest temperature 140 ºC, for 500hours
The protection tube is not damaged
Standard: TL52668