Woven Fabric Abrasion Resistance Heat Shrinkable Tubing

Material(s) Description
Warp material: Polyester
Weft material: Irradiated, modified polyolefin
Coating: Modified polyolefin
Operating temperature range (3000 hours): -40°C to 125°C
Operating temperature range (1000 hours): -40°C to 150°C
Minimum recovery temperature: 110°C
Recommended recovery temperature: 150°C to 200°C
Maximum storage temperature: 50°C
Standard: TL52668 TL52361 D44 1959 GMW14327
Testing organization: CTI PONYProduct description (CL-KSD)Inside diameter (mm)D (min. )expanded as suppliedD (max. )recovered after heatingΦ6/3-B63Φ8/4-B84Φ10/5-B105Φ12/6-B126Φ16/8-B168Φ20/10-B2010Φ25/12-B2512Φ30/15-B3015Φ35/17.5-B3517.5Φ40/20-B4020Φ50/25-B5025Φ60/30-B6030Φ70/35-B7035Φ80/40-B8040Φ100/50-B10050B: BlackOther specifications can be customizedPropertyTest condition(s)PerformanceThermal ageing168 hrs at 125°CNo deterioration in abrasion resistance at 23°C24 hrs at 125°CNo deterioration in abrasion resistance at 23°CFlammabilityMVSS 302Burning rate≤100 mm/minLow temperature flexibility4 hours at -40°C, 10X diameter mandrelNo crackingAbrasion resistance
(1.5N load, 0.3mm radius metal blade, 60 cpm, 50mm stroke, 144 000 cycles)Environmental Chamber Temperature: -35°CNo wear to underlying rubber hoseEnvironmental Chamber Temperature: 140ºCTemperature resistance
1) Test temperature 140 ºC, for 500 hours
2) Remove the sample and cool it to room temperature...Then place the sample at -35°C for 22 hours.
3) Then bend the sample 180 degrees around acylinder with aradius of 30mmTest temperature 140 ºC, for 500 hoursThe protection tube is not damaged
Standard: TL52668