Pad Printing Liquid Silicone for Detailed Patterns Transfering

Liquid Silicone Rubber for Pad Printing application:
Liquid Silicone Rubber for Pad Printing is mainly applicable to making pads for plastics toys, electroplating products, electronic toys, trademarks and irregular pattern printing. Pad printing pads is a carrier which transfer printing the patterns on the steel plate onto the toy products' surface.Liquid Silicone Rubber for Pad Printing features:
Liquid Silicone Rubber for Pad Printing with the advantages of abrasion resistance, high temperature resistance, good printing effect, etc., which made of top-quality raw material due to adding American Dupont Teflon high-temperature resistance new material, is processed through high-temperature machining.Pad printing silicone rubber(HY-916)
Appearance: Yellow, red, green, white
Viscosity(CS): 20000~25000
Hardness(A): 28-30
Tensile strength (kgf/cm) ≥ 35
Tear-strength (kgf/cm) ≥ 24
Elongation break: (%)≥ 400
Retractility (%): ≤ 0.3
Curing agent mixed rate(%): 2-3
Operate time(min): 30
Curing time(hours): 2-4
Operation instruction for Liquid Silicone Rubber for Pad Printing
Admixture amount of curing agent and silicon reaction:
1. Added with 1% of curing agent, silicon can still flow within 2.5 hours, mold can be released in6-8 hours.
2. Added with 2% of curing agent, silicon can still flow within 50 minutes to 1 hour, mold can be released in 2-3 hours.
3. Added with 3% of curing agent, silicon can still flow within 28-30 minutes, mold can be released in 1.5-2 hours
4. Added with 4% of curing agent, silicon can still flow within 10-15 minutes, mold can be released in 1-1.5 hours
5. Curing agent reaction rate is related with weather and temperature. Under 25 degree, they can be added according to the instruction or at double amount in winter or under subzero temperature.
(Note: Curing agent can not be added above the 4% maximum level and the normal proportion is 2%. If more than 4% is applied, the silicon will condensate too fast for normal usage).Above is the mixing data for silicon and curing agent, the precise result of hundreds of times of our experiments. Provided that you arrange production according to our instruction, you are sure to manufacture first class products and maximize your profit this is not only the need of, but also our responsibility for and a satisfactory answer to our customers. We may not be the first, but we will try to be the best. The customers need is what we pursue.Whatever you have any request or questions, pls feel free to email me or call me.SpecialsiliconproductsforpadprintingModel
901#902#912#916#918#928#Appearance
Red
white
Yellow
greenRed
white
Yellow
greenRed
white
Yellow
greenRed
white
Yellow
greenRed
white
Yellow
green
RedMixingproportion
Ofcuringagent2-3%2-3%2-3%2-3%2-3%9:1Operatingtime
(hours)0.50.50.50.50.50.5Curingtime
(hours)3-43-43-43-43-43-4Hardness
(A°)20-2526-3026-3020-2226-3026-28Viscosity
(cs)29000-3400029000-3400029000-3500029000-3500028000-3400029000-35000Tensile-strength
(kgf/cm)≥30≥32≥35≥35≥36≥38Tear-strength
(kgf/cm)≥18≥22≥24≥24≥26≥28Elongation-break
(%)≥360≥380≥410≥420≥420≥450Retractility
(%)≤0.3≤0.3≤0.3≤0.3≤0.3≤0.15Usage
Padprinting
onlyPad
printingonlyPadprintingonlyPadprintingonlyPadprintingonlyPad
printing
onlyPackage
20kg/drumand200kg/drum free sample for your testingIf you want more information about the silicone rubber, pls don't hesitate to contact us: