Peroxide XLPE Insulating Compounds for Wire and Cable

Introduction
XLPE-9101 is composed of low-density polyethylene as basic resin and the addition of crosslinking agents,anti-oxidants and other ingredients. Adopts advanced enclosed mixing device, it does not contain harmful substances such as heavy metals, excellent mechanical properties, electrical properties and heat aging properties, process stability, and the finished surface is smooth, dedicated to the production of MV/HV wires and cables, long-term working temperature is 90 ºC
CharacteristicsProduct NameWires and Cables with XLPE Compounds Rated
Voltages up to and including 10kVSpecifications & ModelsXLPE-9101Characteristics &UsagesApplicable for 10 KV and below cross-linked cablesCharacteristicsAPropertiesUnitRequired ValueTypical valueTest MethodTensile StrengthMPa≥13.519.6GB/T1040.3Elongation at Break%≥350426GB/T1040.3Ageing Property(135±2ºC,168h)GB/T2951.12Variation of Tensile Strength%±20±204GB/T2951.12Variation of Elongation at Break%-2GB/T2951.12Hot Set Test(200±3ºC,0.2Mpa,15min)GB/T2951.21Elongation under load%≤100≤544GB/T2951.21Permanent Elongation after cooling%0GB/T2951.21Low Temperature Brittleness test(-76ºC)Fail data≤15/300GB/T5470Dielectric StrengthMV/m≥2536GB/T1408.1Dielectric Dissipation Factor(50Hz,20ºC)--≤1x10-35x10-4GB/T1409Dielectric Constant
(50Hz,20ºC)--≤2.352.2GB/T1409Volume Resistivity(20ºC)W.m≥1x10148.8x1014GB/T1410Processing:
XLPE-9101, insulation compound is recommended melt extrusion temperature in the range of 90ºC to 120ºC.The specific processing temperature depend on the equipment situation
Storage and Transportation
The product should not be exposed to direct sunlight and rain during transportation and should be stored in clean, cool, dry and ventilated warehouse. Storage should not exceed half year ex-factory. The product is sensitive to water, pay attention to moistureproof.Package